TOP

HOT Type Product Overview

Product Summary

HOT TYPE-1

Product Features

1.At room temperature, the plastic is in block form and is melted in a dedicated tank for dipping parts, etc.
2.After the work, the parts are covered with a plastic film, and oil seeps between the parts and the film to prevent rust.
3.The film's elasticity prevents scratches on parts during storage and transportation.
4.The transparent coating allows for inspection of the product while the parts are still sealed.
5.Since they are packaged exactly the same way as the parts, they can be packed compactly and cushioning materials are no longer needed.
6.Conventional plastic packaging materials require the processing of film, sheets, plates, etc., to make bags, boxes, etc., and then sealing the cut edges.
7.The film can be easily removed by hand without the need for thinner or other chemicals.
8.The removed film can be used (reused) by melting it again.

How to use

Aircraft

Automobile

Vehicles

Spinning machine

Medical instruments

Medical Tools

Packaging of jigs, etc.

Parts for electrical equipment

Film properties

The film formed has the following performance

#011 #011-CN
Tensile strength 22kg/㎠ or more 25kg/㎠ or more
Growth 50% or more 70% or more
Coating speed (reference value) 2.0~2.5mm 2.2~2.8mm
Chemical resistance
1.No change Water, steam, brine, weak acid, weak alkali, alcohol, mineral oil, animal and vegetable oil, various detergents
2.Be slightly soaked Strong alkali, strong acid
3.Be permeated by Organic solvent

Physical and chemical properties

Appearance Yellowish brown translucent body
Specific gravity 0.98
Flammability Wood degree
Toxic None
Melting point 130℃
Flash point 220℃
Point of ignition 550℃
Volatile None

Heating and dissolving

1. Seal peel should be stored in a dedicated tank for proper temperature control.
 Since #151 has poor thermal conductivity and overheating will cause decomposition and performance degradation, please control the temperature of all parts so that the temperature does not exceed 185℃.
 Temperature control also greatly affects the life of the seal peel.
 Also, the tank should be the minimum size necessary.
 A large tank will cause the seal peel to deteriorate easily due to excessive heat load during dissolution, since the seal peel is not metabolized as much.
2. The removed film can be dissolved and used again, but be sure to rinse and dry the removed film thoroughly before reuse.
3. Always keep the area around the tank tidy and supervised.
 Never carry tanks or containers, especially if they are overheated, as this may cause accidents.
4. Take precautions to avoid burns, and if necessary, provide protective equipment.
 Also, be sure to ventilate the room while working.
5. Burnt residue from the raw material may remain in the product, and brown or black particles may be present in the product.
 There will be no problem with product performance if you remove them or use the product as it is.
Translated with www.DeepL.com/Translator (free version)

Wrapping

20kg… Ingot type 1 piece approx. 3kg
1 box packed in corrugated cardboard 20kg
25kg… Ingot type 1 piece approx. 5kg
1 box packed in corrugated cardboard 25kg

How to use

1.[Dissolution] Ingots are cut and put into the dissolution tank.
 Dissolution is heated at a predetermined temperature in a dedicated dissolution tank with a temperature control function.
  (Cutting as finely as possible at this time will shorten the dissolution time.)
2.[Parts are immersed in the dissolved seal peel and immediately removed.
3.[The seal peel resin adhering to the surface by dipping cools immediately upon removal and becomes dry to the touch in tens of seconds to several tens of seconds, depending on the size of the part.
 Several minutes are needed to fully cure.
 The film is highly elastic, and inside the film, rust-preventive oil moderately envelops the metal surface, making the rust-preventive effect of the parts perfect.
 It is also powerful enough to prevent scratches during transportation.
4.[Remove the coating] Most of the gauges such as plug gauges, screw gauges, drills, cutters, etc. can be simply pulled off the coating, which can be used as a protective cap without any modification.
 Depending on the shape of the part, the film can be easily peeled off by cutting a cutter or the like into a portion of the film.

HOT TYPE/TYPE-2

Product Feature

1.At room temperature, the plastic is in block form and is melted in a dedicated tank for dipping parts, etc.
2.The parts are covered with a plastic film and completely sealed from the outside air.
3.The film's toughness prevents scratches on items during storage and transport handling.
4.The film can be easily removed by hand without the need for thinner or other chemicals.

Physicochemical properties

Appearance Red transparent solid
Specific gravity 0.98
Melting point 125℃
Flash point 225℃
Point of ignition 550℃
Volatile None

Heating and dissolving

1. Seal peel should be stored in a dedicated tank for proper temperature control.
 Since #151 has poor thermal conductivity and overheating will cause decomposition and performance degradation, please control the temperature of all parts so that the temperature does not exceed 185℃.
 Temperature control also greatly affects the life of the seal peel.
 Also, the tank should be the minimum size necessary.
 A large tank will cause the seal peel to deteriorate easily due to excessive heat load during dissolution, since the seal peel is not metabolized as much.
2. The removed film can be dissolved and used again, but be sure to rinse and dry the removed film thoroughly before reuse.
3. Always keep the area around the tank tidy and supervised.
 Never carry tanks or containers, especially if they are overheated, as this may cause accidents.
4. Take precautions to avoid burns, and if necessary, provide protective equipment.
 Also, be sure to ventilate the room while working.
5. Burnt residue from the raw material may remain in the product, and brown or black particles may be present in the product.
 There will be no problem with product performance if you remove them or use the product as it is.
Translated with www.DeepL.com/Translator (free version)

Wrapping

25kg Ingot-type
Packing (in cardboard boxes)

How to use

1.[Dissolution] Ingots are cut and put into the dissolution tank.
 Dissolution is performed by heating at a predetermined temperature (180°C) in a dedicated dissolution tank with a temperature control function.
2.[Parts are immersed in the dissolved seal peel and immediately removed.
3.[Drying and curing of the film] The seal peel resin adhering to the surface by immersion cools instantly from the moment it is removed and becomes finger-dry in ten to several dozen seconds, depending on the size of the part.
 It takes several minutes to fully cure. When cutting and removing the coating with a blade, be careful not to lift the remaining coating on the part.
4.[The entire surface of the part is covered with a film, so the film is removed only from the area to be plated.
It can be easily cut and stripped by using a sharp blade (e.g., cutter).
5.[Plating] Since only the parts not to be plated are masked by the above process, they are placed in the cleaning solution, degreasing solution, and plating solution as they are, and the film is peeled off after the process is completed.

How to use the dissolving tank for hot type

How to use

1.Install the tank in a well-ventilated area with no combustible materials around or equipped with a ventilation system, and turn on the power.

2.Cut the seal peel into pieces and feed it in. The smaller the pieces, the less dissolution time, so cut the pieces as small as possible to fill the inner tank to at least the eighth fill position.
If less than this, the upper inner wall will be excessively heated and the seal peel will be seized, which may cause distortion of the inner wall and lead to a fire.

3.When the temperature controller is started, heating is performed at the optimum temperature according to the program.
If the seal peel begins to soften, agitate it in a timely manner.

4.Seal peel liquefies as temperature rises, but the temperature difference between the center and the exterior wall may cause residual melting.
At that time, mix with a clean metal stirring rod to ensure that the mixture is uniform throughout.

5.If the temperature of the liquid is low compared to the temperature setting, such as when the power supply voltage is low, the oil and resin may separate.

6.When the seal peel is heated, air bubbles are generated, but they disappear when the peel is stirred to raise them to the surface, covered, and allowed to sit for a while before starting work.

7.If the working temperature is raised to +10°C or higher, thermal aging will occur and decomposition will begin, resulting in a significant degradation of product performance.

8.If significant white smoke is generated during operation, the temperature is too high. If used as is, it may cause a fire.
As mentioned above, temperature control is the most important factor in seal peel, and it greatly affects product performance and thus usage time.
Please use with caution to avoid burns and fire.

For inquiries about the seal peel HOT type, please contact

Contact us by phone

TEL:045-211-6740(Representative)
FAX:045-211-6741
Office hours: [weekdays].9:00~17:00(JST)

Contact us by e-mail

Mail Form